Roughened printed circuit board

ABSTRACT

A multi-layer structure including a base insulating layer and a thin metal film layer (seed layer) is prepared. A plating resist layer is formed to have a prescribed pattern on the upper surface of the thin metal film layer. A metal plating layer is formed on the thin metal film layer exposed by electroplating. Then, the plating resist layer is removed, and the thin metal film layer in the region having the plating resist layer is removed. In this way, a conductive pattern including the thin metal film layer and the metal plating layer is formed. The upper surface of the base insulating layer in the region without the conductive pattern is subjected to roughening treatment. A cover insulating layer is formed on the upper surfaces of the base insulating layer and the conductive pattern. In this way, a printed circuit board is completed.

BACKGROUND OF THE INVENTION

1. Field of the Invention

The invention relates to a printed circuit board and a manufacturing method thereof.

2. Description of the Related Art

As a method of manufacturing a printed circuit board, a subtractive method, an additive method, and a semi-additive method are known.

For example, a printed circuit board is manufactured according to the subtractive method as follows (see Japanese Patent Laid-Open No. 2002-252257). To start with, a thin metal film is formed as an adhesion promoting layer (seed layer) by sputtering on a base insulating layer such as a polyimide film. Then, a metal plating layer is formed on the thin metal film.

The metal plating layer is then coated with photoresist in a prescribed pattern, followed by drying, and then subjected to process of exposure, development, and etching. Then, the photoresist is removed and a complete conductive (interconnection) pattern forms.

In another example, a printed circuit board is manufactured according to the semi-additive method as follows (see Japanese Patent Laid-Open No. 2002-368393). To start with, a thin copper film is formed on a base insulating layer by sputtering. Then, a plating resist pattern is formed to expose a predetermined interconnection part of the thin copper film. Then, the exposed part of the thin copper film is provided with electrolytic nickel plating, and then the plating resist pattern and the thin copper film in the region of the plating resist pattern are removed. In this way, a complete conductive pattern forms.

In some cases, when the thus produced printed circuit board is used in a high temperature and high humidity atmosphere, ion migration of the conductor (copper in the above example) is caused along the boundary between the base insulating layer and a cover insulating layer formed on a surface of the base insulating layer having the conductive pattern thereon. This short-circuits conductive patterns formed as interconnections.

Herein, the ion migration refers to the movement of metal ions (copper ions in the above example) through water as a medium while an electric field is generated.

SUMMARY OF THE INVENTION

It is an object of the invention to provide a printed circuit board that can sufficiently prevent ion migration of a conductor in a high temperature and high humidity atmosphere and a manufacturing method thereof.

(1) A printed circuit board according to one aspect of the invention includes an insulating layer, and a conductive layer provided on one or both surfaces of the insulating layer and having a prescribed pattern. The region excluding the conductive layer on the surface of the insulating layer that has the conductive layer thereon is roughened.

In the printed circuit board according to the invention, the region excluding the conductive layer is roughened on the surface of the insulating layer having the conductive layer thereon, so that irregularities forms on the insulating layer. In this way, in a high temperature and high humidity atmosphere, the movement of metal ions eluted from the conductive layer is limited by the irregularities on the insulating layer. When another insulating layer is provided to cover the surface of the insulating layer having the conductive layer thereon, the adhesion between these insulating layers improves, and the movement of the metal ions is further limited. Consequently, ion migration of the conductive layer can sufficiently be prevented in the high temperature and high humidity atmosphere.

(2) The conductive layer may include a thin metal film layer provided in contact with the insulating layer. This makes it easier to form a metal plating layer on one or both surfaces of the insulating layer.

(3) The surface roughness of the insulating layer in the region excluding the conductive layer may be at least 0.1 μm. In this way, ion migration of the conductive layer can sufficiently be prevented in a high temperature and high humidity atmosphere.

(4) The conductive layer may include a thin metal film layer provided in contact with the insulating layer, and the surface roughness of the insulating layer in the region excluding the conductive layer may be at least 0.1 μm. The thin metal film layer makes it easier to form a metal plating layer on one or both surfaces of the insulating layer. The surface roughness of the insulating layer in the region excluding the conductive layer is at least 0.1 μm and therefore ion migration of the conductive layer can sufficiently be prevented in a high temperature and high humidity atmosphere.

(5) The insulating layer may have flexibility. In this way, a flexible printed circuit board is manufactured. Therefore, the printed circuit board thus manufactured may find application in various fields of electronic equipment and information related equipment.

(6) A method of manufacturing a printed circuit board according to another aspect of the invention includes the steps of forming a conductive layer having a prescribed pattern on one or both surfaces of an insulating layer, and roughening the region excluding the conductive layer on the surface of the insulating layer having the conductive layer thereon.

By the method of manufacturing a printed circuit board according to the invention, a conductive layer having a prescribed pattern is formed on one or both surfaces of an insulating layer, and the region excluding the conductive layer on the surface of the insulating layer having the conductive layer thereon is roughened.

In this way, the region excluding the conductive layer on the surface of the insulating layer having the conductive layer thereon is roughened, so that irregularities form on the insulating film. Therefore, in a high temperature and high humidity atmosphere, the movement of metal ions eluted from the conductive layer is limited by the irregularities on the insulating layer. When in particular another insulating layer is provided to cover the surface of the insulating layer having the conductive layer thereon, the adhesion between these insulating layers improves, and the movement of the metal ions is further limited. Consequently, ion migration of the conductive layer can sufficiently be prevented in the high temperature and high humidity atmosphere.

(7) The step of roughening the region excluding the conductive layer may include the step of roughening the insulating layer positioned in the region excluding the conductive layer by wet etching, wet blasting, or dry etching process.

In this way, at the time of roughening the insulating layer positioned in the region excluding the conductive layer, the wet etching, wet blasting or dry etching process may selectively be employed depending on the materials of the insulating layer and the conductive layer and the like, so that the region excluding the conductive layer can readily be roughened.

(8) The step of forming a conductive layer having a prescribed pattern may include the step of forming the conductive layer including a thin metal film layer so that the thin metal film layer is in contact with one or both surfaces of the insulating layer. This makes it easier to form a metal plating layer on one or both surfaces of the insulating layer.

According to the invention, the region excluding the conductive layer on the surface of the insulating layer having the conductive layer thereon is roughened, and irregularities form on the insulating layer. In this way, in a high temperature and high humidity atmosphere, the movement of metal ions eluted from the conductive layer is limited by the irregularities on the insulating layer. When in particular another insulating layer is provided to cover the surface of the insulating layer having the conductive layer thereon, the adhesion between these insulating layers improves, and the movement of the metal ions is further limited. Consequently, ion migration of the conductive layer can sufficiently be prevented in the high temperature and high humidity atmosphere.

The foregoing and other objects, features, aspects, and advantages of the present invention will become more apparent from the following detailed description of the present invention when taken in conjunction with the accompanying drawings.

BRIEF DESCRIPTION OF THE DRAWINGS

FIGS. 1( a) to 1(c) are views for use in illustrating a method of manufacturing a printed circuit board according to one embodiment of the invention;

FIG. 2( d) to 2(f) are views for use in illustrating the method of manufacturing the printed circuit board according to the embodiment of the invention;

FIGS. 3( g) and 3(h) are views for use in illustrating the method of manufacturing the printed circuit board according to the embodiment of the invention; and

FIGS. 4( a) and 4(b) are schematic views of printed circuit boards according to Inventive Example 1 and Comparative Example 1.

FIG. 5 is a schematic view of a printed circuit board similar to FIG. 4( a) according to another embodiment of the invention with a conductive layer on each surface of the insulating layer.

DESCRIPTION OF THE PREFERRED EMBODIMENTS

Now, a printed circuit board according to one embodiment of the invention and a manufacturing method thereof will be described. In the following description, the printed circuit board refers for example to a printed circuit board having flexibility (flexible printed circuit board).

FIG. 1( a) to FIG. 3( h) are views for use in illustrating a method of manufacturing a printed circuit board according to the embodiment.

As shown in FIG. 1( a), a multi-layer structure including a base insulating layer 1 having a thickness of 5 μm to 50 μm and a thin metal film layer (seed layer) 2 having a prescribed thickness is prepared. The base insulating layer 1 has flexibility. Note that the base insulating layer 1 preferably has a thickness from 10 μm to 30 μm.

As shown in FIG. 1( b), a plating resist layer 3 for example of photosensitive resin is formed on one surface (hereinafter referred to as “upper surface”) of the thin metal film layer 2. Then, as shown in FIG. 1( c), the plating resist layer 3 is subjected to exposure and development process using a prescribed pattern. In this way, the plating resist layer 3 having the prescribed pattern is formed on the thin metal film layer 2. Then, the part of the thin metal film layer 2 corresponding to the interconnection pattern is exposed.

Note that the plating resist layer 3 may be formed of a material other than the photosensitive resin as far as the material can be formed into the prescribed pattern on the thin metal film layer 2.

Then, as shown in FIG. 2( d), a metal plating layer 4 is formed on the thin metal film layer 2 exposed by electroplating. The metal plating layer 4 may be for example of nickel, copper, gold, or a solder material.

As shown in FIG. 2( e), the plating resist layer 3 is removed, and the thin metal film layer 2 in the region of the plating resist layer 3 is removed. In this way, as shown in FIG. 2( f), conductive patterns HP including the thin metal film layer 2 and the metal plating layer 4 are formed. The conductive patterns HP preferably have a thickness in the range from 5 μm to 30 μm, more preferably from 5 μm to 15 μm. When the conductive patterns HP are sufficiently thin, the resulting printed circuit board has flexibility.

Now, according to the embodiment, as shown in FIG. 3( g), the upper surface of the base insulating layer 1 in a region S without the conductive patterns HP is roughened. The surface may be roughened for example by wet etching or wet blasting process using an acid or alkaline liquid. Dry etching process such as sputtering and plasma etching may be employed.

The surface roughness of the region S resulting from the roughing process is preferably in the range from 0.1 μm to 0.5 μm. The surface roughness is based on the surface roughness (Ra) defined by “JIS (Japanese Industrial Standard) B0601.”

As shown in FIG. 3( h), a cover insulating layer 5 is then formed on the upper surface of the base insulating layer 1 and on the conductive patterns HP. The thickness of the cover insulating layer 5 is preferably in the range from 3 μm to 30 μm, more preferably from 5 μm to 30 μm.

In this way, the printed circuit board 10 according to the embodiment is completed.

In the printed circuit board 10 described above, an adhesive layer may be provided as required between the base insulating layer 1 and the conductive patterns HP and between the conductive patterns HP and the cover insulating layer 5. In this case, the thickness of the adhesive layer is preferably in the range from 5 μm to 50 μm, more preferably from 10 μm to 20 μm.

The conductive patterns HP of the printed circuit board 10 have a two-layer structure including the thin metal film layer 2 and the metal plating layer 4, but the conductive patterns HP may have a single-layer structure or a multi-layer structure consisting of two or more layers.

In the foregoing, how the conductive patterns HP are formed by the semi-additive method has been described, while the conductive patterns HP may be formed either by the additive method or the subtractive method.

In the printed circuit board 10 according to the embodiment, the region S of the base insulating layer 1 having the conductive patterns HP thereon is roughened excluding the location of the conductive patterns HP, so that irregularities form on the base insulating layer 1. In a high temperature and high humidity atmosphere, the movement of metal ions (copper ions) eluted from the conductive patterns HP is limited by the irregularities on the base insulating layer 1. According to the embodiment, the cover insulating layer 5 is provided on the surface of the base insulating layer 1 having the conductive patterns HP thereon to cover the surface, so that the base insulating layer 1 and the cover insulating layer 5 are more tightly adhered with each other, which further limits the movement of the metal ions. Consequently, ion migration in the conductive patterns HP can sufficiently be prevented in the high temperature and high humidity atmosphere.

As described above, according to the embodiment, the conductive patterns HP include the thin metal film layer 2 provided in contact with the base insulating layer 1. In this way, the thin metal film layer 2 makes it easier to form the metal plating layer 4 on one or both surfaces of the base insulating layer 1.

The surface roughness of the base insulating layer 1 in the region S excluding the conductive patterns HP is preferably not less than 0.1 μm. In this way, ion migration in the conductive layer can sufficiently be prevented in the high temperature and high humidity atmosphere.

Note that no surface roughening treatment is carried out to the region other than the region S on the upper surface of the base insulating layer 1, in other words, to the region where the conductive patterns HP are formed. In this way, there is no irregularity at the interface between the base insulating layer 1 and the conductive patterns HP, so that the transmission loss regarding electrical signals at the surface of the conductive patterns HP can be reduced.

Furthermore, when the conductive patterns HP are formed on the upper and lower surfaces of the base insulating layer 1, as seen in FIG. 5, the base insulating layer 1, positioned between the upper and lower conductive patterns HP, serves as a capacitor. In this case, the presence of irregularities at the interface between the base insulating layer 1 and the conductive patterns HP would cause variation in the capacitance value. This makes designing of the printed circuit board 10 difficult.

In contrast, in the printed circuit board 10 according to the embodiment, there is no irregularity at the interface between the base insulating layer 1 and the conductive patterns HP, and therefore variation is not caused in the capacitance value of the base insulating layer 1. Consequently, designing of the printed circuit board 10 is easy.

According to the embodiment, the thin metal film layer 2 is formed as a part of the conductive patterns HP on the base insulating layer 1. By the semi-additive method as described above in general, the thin metal film layer 2 is formed on the base insulating layer 1 in order to form the metal plating layer 4 for the conductive patterns HP.

In the printed circuit board 10 according to the embodiment, irregularities are formed on the base insulating layer 1 between the conductive patterns HP, and therefore the movement of eluted metal ions is prevented by the irregularities on the base insulating layer 1. As a result, ion migration of the conductive patterns HP can sufficiently be prevented.

Therefore, the invention is particularly advantageously applied to the printed circuit board 10 having the thin metal film layer 2 as the conductive patterns HP.

In the printed circuit board according to the embodiment, the conductive patterns HP correspond to the conductive layer.

EXAMPLES

Now, printed circuit boards according to Inventive Example 1 and Comparative Example 1 were produced based on the printed circuit board and the manufacturing method thereof as described above.

FIG. 4( a) is a schematic sectional view of a printed circuit board 10 according to Inventive Example 1, and FIG. 4( b) is a schematic sectional view of a printed circuit board 20 according to Comparative Example 1.

Inventive Example 1

When the printed circuit board 10 according to Inventive Example 1 was produced, conductive patterns HP were formed according to the semi-additive method similarly to the above example, details of which will be described.

To start with, a polyimide resin film having a thickness of 25 μm was prepared as a base insulating layer 1. A sputtering film of nickel and a sputtering film of copper were formed as a thin metal film layer 2 on the upper surface of the base insulating layer 1 by continuous sputtering. In this case, the nickel sputtering layer had a thickness of 30 nm and the copper sputtering film had a thickness of 200 nm.

Then, a plating resist layer 3 made of photosensitive resin was formed on the upper surface of the thin metal film layer 2. Then, the plating resist layer 3 was subjected to exposure and development treatment using a prescribed pattern. In this way, the plating resist layer 3 having the prescribed pattern was formed on the thin metal film layer 2.

Then, a copper plating layer having a thickness of 10 μm was formed as a metal plating layer 4 on the thin metal film layer 2 exposed by the electroplating. Then, the plating resist layer 3 was removed and the thin metal film layer 2 in the region of the plating resist layer 3 was removed.

In this way, conductive patterns HP including the thin metal film layer 2 and the metal plating layer 4 were formed.

Then, roughening treatment was carried out to the upper surface of the base insulating layer 1 in the region S without the conductive patterns HP. The roughening treatment was performed by plasma etching.

Plasma system PWB-4 manufactured by APS Corporation was used. As the treatment conditions, the frequency was set to 40 kHz and the gas ratio between oxygen and argon was set to be 50%:50%. The pressure was set to 200 mTorr, the power was set to 3000 W, and the electrode temperature was set to 45° C.

After the roughening treatment described above, the surface roughness in the region S of the base insulating layer 1 was 0.1 μm. Note that the surface roughness was based on the surface roughness (Ra) defined by “JIS (Japanese Industrial Standard) B0601.”

Finally, a polyimide resin film having a thickness of 25 μm was attached as a cover insulating layer 5 to the base insulating layer 1 and the upper surface of the conductive patterns HP through an adhesive layer having a thickness of 15 μm. In this way, the printed circuit board 10 according to Inventive Example 1 was completed.

Comparative Example 1

The printed circuit board 20 according to Comparative Example 1 is different from the printed circuit board 10 according to Inventive Example 1 in the following points. As shown in FIG. 4( b), in the printed circuit board 20 according to Comparative Example 1, the region S on the upper surface of the base insulating layer 1 was not subjected to the roughening treatment.

Evaluation

The printed circuit boards 10 and 20 according to Inventive Example 1 and Comparative Example 1 were kept in an atmosphere at a temperature of 60° C. and a humidity of 95% while a voltage at 30 V continued to be applied, and variation in the insulation resistance value between conductive patterns HP with time was measured. The measurement was carried out using an ion migration evaluation system manufactured by Espec Corporation.

In the above described high temperature and high humidity atmosphere, the initial insulation resistance values in Inventive Example 1 and Comparative Example 1 were both 1×10⁹ Ω.

The insulation resistance value between the conductive patterns HP according to Inventive Example 1 was 1×10⁸ Ω or more after 1000 hours. In contrast, the insulation resistance value between the conductive patterns HP according to Comparative Example 1 was 1×10⁶ Ω or lower after 100 hours, and an insulation failure was caused.

As can be understood from the results, it can be considered that when the region S on the upper surface of the base insulating layer 1 is subjected to roughening treatment, the movement of metal ions (copper ions) eluted from the conductive patterns HP is prevented by the irregularities on the base insulation layer 1, in other words, ion migration by the conductive patterns HP can be prevented. The cover insulating layer 5 is provided to cover the surface of the base insulating layer 1 having the conductive patterns HP thereon, so that the adhesion between the base insulating layer 1 and the cover insulating layer 5 improves, which can further prevent the movement of metal ions.

Although the present invention has been described and illustrated in detail, it is clearly understood that the same is by way of illustration and example only and is not to be taken by way of limitation, the spirit and scope of the present invention being limited only by the terms of the appended claims. 

1. A printed circuit board, comprising: a first insulating layer; and a conductive layer comprising a conductive material, provided on one or both surfaces of said first insulating layer and having a prescribed pattern, the one or both surfaces of said first insulating layer comprising at least one area where the conductive material is present and at least one area where the conductive material is not present, wherein the area where the conductive material is not present has a surface roughness of at least 0.1 μm, and wherein the surface roughness Ra of the first insulating layer in the area where the conductive material is not present is greater than the surface roughness Ra of the first insulating layer in the area where the conductive material is present and the surface roughness of the conductive layer.
 2. The printed circuit board according to claim 1, wherein said conductive layer comprises a thin metal film layer provided in contact with said first insulating layer.
 3. The printed circuit board according to claim 1, wherein said first insulating layer has flexibility.
 4. The printed circuit board according to claim 1, further comprising a second insulating layer covering the first insulating layer and the conductive layer.
 5. A printed circuit board, comprising: a first insulating layer, a conductive layer provided on at least one surface of said first insulating layer, and having a prescribed pattern, and a second insulating layer provided on said one surface of said first insulating layer so as to cover said conductive layer, wherein said conductive layer has a first surface being in contact with said one surface of said first insulating layer, and a second surface being in contact with said second insulating layer, said one surface of said first insulating layer includes a first region where said conductive layer is present, and a second region where said conductive layer is not present, and said second region is roughened to have a surface roughness of at least 0.1 μm such that the surface roughness Ra of said first insulating layer in said second region is greater than the surface roughness Ra of said first insulating layer in said first region and the surface roughness of the first and second surfaces of said conductive layer.
 6. The printed circuit board according to claim 5, wherein said conductive layer comprises a thin metal film layer provided in contact with said first insulating layer.
 7. The printed circuit board according to claim 5, wherein said first and second insulating layers have flexibility. 